性能项目
|
试验条件[状态]
|
测试方法
|
测试数据
|
数据单位
|
|
吸水率
|
24小时浸渍(23℃)
|
ASTM D-570
|
DAM｜50%RH,1.2｜-
|
%
|
|
吸水率
|
饱和(23℃)
|
ASTM D-570
|
DAM｜50%RH,8.5｜-
|
%
|
|
比重
|
|
ASTM D-792
|
DAM｜50%RH,1.14｜1.14
|
|
泰伯磨耗量
|
cs-17 Wheel 1000g
|
|
DAM｜50%RH,-｜7
|
mg/1000 cycles
|
|
埃佐冲击强度
|
23℃
|
ASTM D-256
|
DAM｜50%RH,53｜112
|
j/m
|
|
洛氏硬度M
|
|
ASTM D-785
|
DAM｜50%RH,M79｜M59
|
|
硬度计硬度
|
|
ASTM D-676
|
DAM｜50%RH,89｜82
|
|
洛氏硬度R
|
|
ASTM D-785
|
DAM｜50%RH,R121｜R108
|
|
屈服强度
|
23℃
|
|
DAM｜50%RH,82.7｜58.6
|
MPa
|
|
拉伸强度
|
23℃
|
ASTM D-638
|
DAM｜50%RH,82.7｜77.2
|
MPa
|
|
揉曲模量
|
23℃
|
ASTM D-790
|
DAM｜50%RH,2827｜1207
|
MPa
|
|
拉伸冲击强度
|
短试样23℃
|
ASTM D-1822
|
DAM｜50%RH,157｜231
|
KJ/m2
|
|
1%形变时的压应力
|
|
ASTM D-695
|
DAM｜50%RH,33.8｜-
|
MPa
|
|
剪切强度
|
23℃
|
ASTM D-732
|
DAM｜50%RH,66.2｜-
|
MPa
|
|
断裂伸长率
|
23℃
|
ASTM D-638
|
DAM｜50%RH,60｜≥300
|
%
|
|
屈服伸长率
|
|
ASTM D-638
|
DAM｜50%RH,5｜25
|
%
|
|
拉伸冲击强度
|
长试样23℃
|
ASTM D-1822
|
DAM｜50%RH,504｜1470
|
KJ/m2
|
|
介电常数
|
106Hz(cps)
|
ASTM D-150
|
DAM｜50%RH,3.6｜4.6
|
|
耗散因数
|
100Hz(cps)
|
ASTM D-150
|
DAM｜50%RH,0.01｜0.2
|
|
介电常数
|
103Hz(cps)
|
ASTM D-150
|
DAM｜50%RH,3.9｜7.0
|
|
耗散因数
|
106Hz(cps)
|
ASTM D-150
|
DAM｜50%RH,0.02｜0.1
|
|
耗散因数
|
103Hz(cps)
|
ASTM D-150
|
DAM｜50%RH,0.02｜0.2
|
|
体积电阻率
|
|
ASTM D-257
|
DAM｜50%RH,10,15,｜10,13
|
Ω.cm
|
|
介电常数
|
100Hz(cps)
|
ASTM D-150
|
DAM｜50%RH,4.0｜8.0
|
|
荷重形变
|
13.8MPa，50℃
|
ASTM D-621
|
DAM｜50%RH,1.4｜-
|
%
|
|
热畸变温度
|
18×106Pa
|
ASTM D-648
|
DAM｜50%RH,90｜-
|
℃
|
|
熔点结晶
|
|
ASTM D-2177
|
DAM｜50%RH,270｜-
|
℃
|
|
UL可燃性导级
|
|
UL 94
|
DAM｜50%RH,94｜V-2
|
|
脆化温度
|
|
ASTM D-746
|
DAM｜50%RH,-80｜-65
|
℃
|
|
热畸变温度
|
(0.5)×106Pa
|
ASTM D-648
|
DAM｜50%RH,235｜-
|
℃
|
|
导热系数
|
|
|
DAM｜50%RH,0.25｜-
|
w/mk
|
|
线性热膨胀系数
|
|
ASTM D-696
|
DAM｜50%RH,7×10,-5,｜-
|
m/m/℃
|
|
熔点
|
Fisher Johns法
|
ASTM D-789
|
DAM｜50%RH,255｜255
|
℃
|
|
需氧指数
|
|
ASTM D-2863
|
DAM｜50%RH,28｜31
|
%
|
|